8x KNAUF Insulation Haftklebeband LDS Soliplan 60mm 40m

KNAUF Insulation Adhesive Tape LDS Soliplan 60mm 40m

For permanently airtight bonding of overlaps and joints in interior areas, part of the Knauf Insulation Airtightness System certified for its long-term functionality and aging resistance

Advantages:

• Optimal for vapor barrier membranes and wood-based panels such as OSB
• Especially high tack and aging resistant
• Easy to process by hand tearing
• Free of solvents
• According to DIN 4108 Part 7, SIA 180, O?NORM B 81102, EnEV, ETAG 007

Product description:
Adhesive tape based on kraft paper for overlapping vapor barrier membranes and airtightness layers according to DIN 4108 Part 7, SIA 180, O?NORM B 81102, EnEV, ETAG 007, as well as for connection bonding on suitable substrates, part of the Knauf Insulation Airtightness System certified for its long-term functionality and aging resistance

Aging resistance of the bonds:
Properly bonded joints with the certified system components are highly aging resistant > 50 years; test report University of Kassel and thus meet the requirements of ETAG 007 guideline for European technical approval; ETAG 007 guideline for timber frame construction joints

Suitable bonding substrates:

• LDS System vapor barrier membranes
• Polyamide and aluminum foils as well as polyethylene foils according to DIN EN 13984
• Polypropylene spunbond membranes according to DIN EN 13984 and DIN EN 13859
• Kraft paper
• Wood-based panels with a solid surface, e.g., panels made of long, flat, aligned chips such as OSB according to DIN EN 300
• Corrosion-free metal substrates and planed wooden components indoors

The applicable processing guidelines must be observed

Substrate condition :
The bonding substrate must be load-bearing, dry, clean, free of sand, dust, grease, and silicone. Non-certified substrates must be checked for their adhesion suitability before starting work; if necessary, adhesion tests should be carried out. Bonding on frozen or overly frozen substrates is not possible. Outgassing release agents, slip agents, and flame retardants on foil surfaces can reduce the aging resistance of the bond.