PCI Nanocret FC Concrete Putty 5 kg Bag

PCI Nanocret FC low-voltage weather-resistant and weather-resistant concrete filler fiber-reinforced

Product features

• Low-voltage, durable, weather and frost-resistant
• Universal for interior and exterior use
• Becomes plastic and easy to work with after water addition
• Fast setting, yet approximately 45 minutes processing time
• Fine-grained surface, no overcoating necessary
• Machine and hand processable
• Tested according to DAfStb guideline for the protection and repair of concrete components
• Certified according to EN 15043 R2

Colors: gray, gray-brown

Packaging options: 25kg sack, 5kg bag

Application area

• For interior and exterior use
• For wall and ceiling
• For repairing gravel nests, filling cavities
• For overcoating masonry and cement plaster
• As concrete filler on concrete, visible and porous concrete
• For leveling uneven wall surfaces prior to tile and slab installation
• As leveling mortar in swimming pools
• Fine plaster after concrete restoration with PCI Peciment 50 on vertical and non-trafficable exposed concrete surfaces in engineering and bridge construction according to ZTVING for the application case PCC II (non-trafficable surfaces subjected to dynamic loads, e.g., bridge undersides)
• As fine plaster for OS4 or OS 5a coatings according to DAfStb
• For layer thicknesses of 1 to 10 mm

Substrate preparation

The substrate must be clean, firmly bonded, open-pored, absorbent, and sufficiently rough. The minimum quality standards for concrete substrates must meet C20/25. Extremely dense, smooth substrates, as well as non-load-bearing layers such as foamed concrete surfaces, must be removed using suitable methods such as shot blasting with fixed abrasive media or high-pressure water jetting.

The adhesion tensile strength of a prepared concrete substrate must not be less than 0.8 N/mm².

The pretreated substrate should be sufficiently moist and kept moist for at least 2 hours before applying PCI Nanocret FC. The surface must be matt and moist.

Priming

On absorbent cementitious substrates, the substrate can be troweled without primer if pre-moistened to a matte, moist state.

Highly absorbent substrates, e.g., porous concrete, should be pre-moistened or primed with PCI Gisogrund 1, diluted 1:1 to 1:2 with water.

Smooth, absorbent substrates should be primed with PCI Gisogrund 1, diluted 1:1 with water. Non-absorbent substrates should be primed with PCI Gisogrund 303.

Application of PCI Nanocret FC

Mix approximately 55% of the cold, clean mixing water in a suitable container. Then add 25 kg PCI Nanocret FC and mix for 3 minutes to a lump-free, plastic mortar. Larger quantities can be mixed in a forced-action mixer.

After a maturation time of about 3 minutes, remix PCI Nanocret FC.

The mortar can be processed using standard techniques such as troweling with a steel trowel—first apply a contact layer to the substrate. Small gaps can be filled with a steel trowel, larger surfaces leveled with a straightedge in horizontal and vertical directions.

For machine application via spraying, first spray a thin contact layer, then apply PCI Nanocret FC in the desired layer thickness.

After the mortar has set, approximately 45 to 90 minutes depending on substrate and processing temperature, PCI Nanocret FC can be smoothed with damp Styrofoam, a cloth, or a sponge board without additional water.

In high temperatures, wind exposure, and direct sunlight, the mortar should be protected from rapid drying, e.g., by misting with water multiple times, covering with jute mats or PE foil.

Safety Data Sheet

Arbeitsschutz und Lagerung

Storage classes

Hazard

Signal word	Danger
GHS pictogram
GHS pictogram
Hazard statements	H315 Causes skin irritation H318 Causes serious eye damage H335 May cause respiratory irritation

Ingredients